ArticleName Comparative analysis of copper wire properties after strand-type and conveyor annealing
ArticleAuthor Loginov Yu. N., Demakov S. L., Illarionov A. G., Stepanov S. I., Kopylova T. P.
ArticleAuthorData

Institute of Materials Science and Metallurgy, Ural Federal University named after the first President of Russia B. N. Yeltsin, Ekaterinburg:

Yu. N. Loginov, Professor, e-mail: j.n.loginov@urfu.ru

S. L. Demakov, Assistant Professor

A. G. Illarionov, Assistant Professor

S. I. Stepanov, Researcher

 

Ural Mining-Metallurgical Company, JSC “Joint Enterprise “Katur-Invest”, Verkhnyaya Pyshma, Russia:

T. P. Kopylova, Technologist

Abstract

The purpose of this work is definition of differences in impact of strand-type and conveyor annealing for thermal copper wire treatment. Batch of industrial and laboratory experiments with copper wire, obtained by rod drawing, was carried out for comparison of strand-type and conveyor annealing effect. Wire with 2 mm diameter was manufactured at two enterprises, using drawing mills, operating in sliding mode. Deformation degree was 2.8, and relative cross-sectional area reduction was 94%. The strand-type annealing was carried out with resistive annealing adapter, mounted into working line of drawing machine with drawing speed of 18 m/s. Thermal effect time was 0.015 s. In the second method, annealing was carried out in conveyor electrical resistance furnace in water vapor atmosphere during 59 minutes. Both methods were characterized by similar values of tensile strength and contraction ratio. Tensile strength was increased with respect to hot-rolled condition from 240 MPa to 260 MPa, which can be explained by grain structure grinding and texture state change. At the same time, the yield strength was decreased from 142 MPa to 108 MPa (by 24%). Next batch of experiments was set with energy changing, where short strand-type annealing was carried out with changing of current in machine annealing adapter with drawing of wire with diameter of 1.78 mm at a speed of 25 m/s. Annealing current density was stepwise changed from 691 to 731 A/mm2. After drawing, testing samples were selected and mechanical properties were determined by sample tension. Dependence of tensile strength function on current density was poorly defined with a minimum difference of maximum and minimum values at the level of ~4%. More signified minimum at the current density of 715 A/mm2 was observed for conditional yield strength. Maximum value (149 MPa) differed from minimum value (133 MPa) by 11%. Maximum elongation of 38% was reached at the same current density. Thus, it is shown that increase of plastic properties can be reached by either conveyor annealing, or optimization of current density in strand-type annealing operation. With respect to the strand-type annealing, conveyor annealing makes a slightly lower tensile strength of copper possible, and significantly reduces yield strength. Minimum strength properties and maximum plastic properties were reached at a current density of 715 A/mm2.

Authors express their gratitude for financial support of the development programs of Ural Federal University, and support of leading Russian Universities for increasing of their competitiveness No. 211 of the Government of Russian Federation No.02.A03.21.0006, and Ministry of Education and Science of Russian Federation, within the realization of the state task of Ural Federal University No. 2014/236.

keywords Copper wire, drawing, annealing, strength, flexibility, strain, current density
References

1. Kolachev B. A., Elagin V. I., Livanov V. A. Metallovedenie i termicheskaya obrabotka tsvetnykh metallov i splavov (Metal science and thermal treatment of non-ferrous metals and alloys). Moscow : MISiS, 1999. 414 p.
2. Loginov Yu. N., Inatovich Yu. V., Zuev A. Yu. Issledovanie kontaktnogo treniya pri nepreryvnoy goryachey prokatke katanki iz elektrotekhnicheskoy medi (Research of contact friction with continuous hot rolling of electrotechnical copper rod). Proizvodstvo Prokata = Rolled Products Manufacturing. 2010. No. 2. pp. 14–19.
3. Loginov Yu. N., Demakov S. L., Illarionov A. G., Ivanova M. A., Romanov V. A. Struktura sostoyaniya mednoy katanki, poluchennoy pri nepreryvnom protsesse litya — prokatki (Structure of state of copper rod, obtained in the time of continuous casting-rolling process). Tsvetnye Metally = Non-ferrous metals. 2013. No. 8. pp. 87–92.
4. Inakazu N., Kaneno Y., Inoue H. Fiber texture formation and mechanical properties in drawn fine copper wire. Materials Science Forum. 1994. Vol. 157–162. pp. 715–720.
5. Loginov Yu. N., Demakov S. L., Illarionov A. G., Popov A. A. Effect of the Strain Rate on the Properties of Electrical Copper. Russian Metallurgy (Metally). 2011. Vol. 3. pp. 194–201.
6. Wright R. N. Secondary recrystallization in heavily drawn ETP copper wire. Metallurgical Transactions A. 1976. Vol. 7, Iss. 12. pp. 1891–1896.
7. Demakov S. L., Loginov Yu. N., Illarionov A. G., Ivanova M. A., Karabanalov M. S. Effect of annealing temperature on the texture of copper wire. The Physics of Metals and Metallography. 2012. Vol. 113, No. 7. pp. 681–686.
8. Baudin T., Etter A. L., Penelle R. Annealing twin formation and recrystallization study of cold-drawn copper wires from EBSD measurements. Materials Characterization. 2007. Vol. 58, Iss. 10. pp. 947–952.
9. Xu Zh., Tang G., Tian Sh., He J. Research on the engineering application of multiple pulses treatment for recrystallization of fine copper wire. Materials Science and Engineering A. 2006. Vol. 424. pp. 300–306.
10. Smiryagin A. P., Smiryagina N. A., Belova A. V. Promyshlennye tsvetnye metally i splavy (Industrial non-ferrous metals and alloys). Moscow : Metallurgiya, 1974. 488 p.
11. Osintsev O. E., Fedorov V. N. Med i mednye splavy. Otechestven nye i zarubezhnye marki : spravochnik (Copper and copper alloys. Russian and foreign grades : reference book). Moscow : Mashinostroenie, 2004. 336 p.

Language of full-text english
Full content Buy
Back