Journals →  Tsvetnye Metally →  2014 →  #1 →  Back

HEAVY NON-FERROUS METALS
ArticleName Interaction between sulphide nickel concentrate and sodium chloride in the temperature range of up to 600 oC
ArticleAuthor Medvedev A. S., Aleksandrov P. V., Imideev V. A.
ArticleAuthorData

Chair of Non-Ferrous Metals and Gold, National University of Science and Technology “MISiS”, Moscow, Russia:

A. S. Medvedev, Professor, e-mail: medvedev@splav.dol.ru
P. V. Aleksandrov, Senior Lecturer
V. A. Imideev, Post-Graduate Student

Abstract

The prospectiveness of low-temperature roasting of sulphide nickel raw materials with alkaline metal chlorides is caused by reduction of SO2 discharge into the air and formation of watersoluble nickel compounds during roasting. NiCl2, NiSO4 and NiO were defined as thermodynamic feasible products of reaction between nickel sulphide and sodium chloride in the presence of oxygen. Solid products of interaction of nickel sulphide concentrate with sodium chloride in the presence of oxygen were experimentally established by X-ray diffraction analysis. There was experimentally determined, that in case of roasting of nickel sulphide concentrate without NaCl in the temperature of 450 oС, nickel is mostly included in residue in sulphide form. In case of roasting with sodium chloride, nickel sulphide wasn’t found in residue. Unfortunately, water-soluble compounds of molybdenum in residue weren’t identified by X-ray diffraction analysis (neither sulphate no chloride), which probably reason is amorphous form of water-soluble compounds. Mixture of concentrate and sodium chloride was roasted in the temperature range of 300–600 oС with further leaching of solid residue by water and sulphuric acid in order to determine the optimal temperature of roasting with NaCl. Best results were achieved by roasting of nickel sulphide concentrate with sodium chloride in the temperature range of 350–400 oС. Under these conditions, it is possible to recover 85% of Ni and 96% of Ni by water and acid leaching, respectively. In order to decrease the sulphuric acid consumption, it is reasonable to arrange water and acid leaching process stages.

keywords Nickel sulphide, low-temperature roasting, sodium chloride, water-soluble, extraction, nickel concentrate, roasting products
References

1. Medvedev A. S., So Tu, Hamhash A., Ptitsyn A. M. Tsvetnye Metally — Non-ferrous metals. 2010. No. 1. pp. 33–36.
2. Chakravortty M., Srikanth S. Kinetics of salt roasting of chalcopyrite using KCl. Thermochimica Acta. 2000. Vol. 362, No. 1/2. pp. 25–35.
3. Chakravortty M., Srikanth S. Non-isothermal thermoanalytical studies on the salt roasting of chalcopyrite using KCl. Thermochimica Acta. 2001. Vol. 370, No. 1/2. pp. 141–148.
4. Bayer G., Wiedemann H. G. Thermal analysis of chalcopyrite roasting reactions. Thermochimica Acta. 1992. Vol. 198, No. 2. pp. 303–312.
5. Medvedev A. S., Aleksandrov P. V., Kadirov A. A. Tsvetnye Metally — Non-ferrous metals. 2012. No. 12. pp. 74–77.
6. Maslenitskiy I. N., Chugaev L. V., Borbat V. F. et al. Metallurgiya blagorodnykh metallov : uchebnik dlya vuzov (Metallurgy of noble metals : tutorial for universities). Moscow : Metallurgiya, 1987. pp. 280–281.
7. Ngoc N. V., Shamsuddin M., Prasad P. M. Salt roasting of an off-grade copper concentrate. Hudrometallurgy. 1989. Vol. 21, No. 3. pp. 359–372.
8. Babenko A. R., Smirnov V. I. Izvestiya vuzov. Tsvetnaya metallurgiya — Russian Journal of Non-Ferrous Metals. 1970. No. 3. pp. 34–39.

Language of full-text russian
Full content Buy
Back