ArticleName |
Influence of hot isostatic pressing on structure, phase composition and mechanical properties of intermetallic compounds on the base of Ti – Al – Nb – Mo – Cr – Zr system |
ArticleAuthorData |
А. A. Baikov Institute of Metallurgy and Materials Science1, Moscow, Russia ; National University of Science and Technology “MISiS”2, Moscow, Russia:
T. K. Akopyan, Researcher1,2, e-mail: aktorgom@gmail.com
National University of Science and Technology “MISiS”, Moscow, Russia: N. A. Belov, Deputy Director of Engineering Center “Casting Technologies and Materials”, Professor of a Chair of Casting Technologies and Metal Art A. S. Aleshchenko, Assistant Professor of a Chair of Metal Forming N. O. Korotkova, Post-Graduate Student |
Abstract |
The phase composition and structure of the TNM type γ-alloys have been analyzed applied to the hot isostatic pressing (HIP) temperature, using both computational and experimental methods. The thermodynamic analysis of the investigated -alloys (TNM (% (at.): 42.99 Al, 4.52 Nb and 1.07 Mo) and TNM+ (% (аt.): 43.01 Al, 4.31 Nb, 1.02 Mo, 0.9 Cr and 0.92 Zr), has been performed using the Thermo-Calc software and has revealed that the temperature of 1250 оC can be considered as optimal for HIP-treatment, from the position of their phase relationship at this temperature. The experimental studies of the alloys microstructure in as-cast state and after conventional vacuum annealing at 1250 оC have showed that γ/α2-colonies which were formed as a result of the eutectoid decomposition of the α-phase are the main structural component. The particles of the β- and γ-phases are identified at the boundaries of these colonies. The HIP-treatment of the basic TNM alloy at 1250 оC and overpressure of 170 MPa does not lead to quantitative changes in the phase composition in comparison to the vacuum annealing, however, coarsening of the eutectic colonies is observed. The HIP-treatment of the TNM+ alloy leads to significant changes of phase relationship as compared to the vacuum annealing, in particular, the amount of γ-phase increases substantially (from 15 to 51 % (vol.), while the amount of -phase decreases from 65 to 17 % (vol.). The hardness (HV 10) of TNM alloy after HIP and conventional annealing is not different, and is about 385 units. The high content of γ-phase in the TNM+ alloy after HIPtreatment reduces its hardness by ~30 units as compared with vacuum annealing, and it makes approximately 330 units. The uniaxial compression tests of alloys after HIP-treatment have showed that the yield stress (σ0.2) of TNM alloy is slightly higher than that of TNM+ alloy (840 MPa against 787 MPa). This result is also explained by the increased amount of soft γ-phase in the TNM+ alloy. Minimum standard deviation of yield strength is noted for both alloys, which is connected with a positive effect on the HIP-treatment on the mechanical properties reproducibility. The work has been conducted under support of the Russian Foundation of Basic Research, the grant for the scientidic project No. 16-33-01108 “Development of physical and chemical grounds for control of phase composition, structure and properties of the prospective alloys based on titanium aluminides”. |
References |
1. Appel F., Paul J. D. H., Oehring M. Gamma Titanium Aluminide Alloys: Science and Technology. Weinheim : Wiley-VCH Verlag & Co, KGaA, 2011. 745 р. 2. Ilin A. A., Kolachev B. A., Polkin I. S. Titanovye splavy. Sostav, struktura, svoystva : spravochnik (Titanium alloys. Composition, structure, properties : reference book). Moscow : All-Russia Institute of Light Alloys-Moscow State Aviation Technological University, 2009. 520 p. 3. Xinhua Wu. Review of alloy and process development of TiAl alloys // Intermetallics. 2006. Vol. 14, No. 10/11. Р. 1114–1122. 4. Hu D., Wu X., Loretto M. H. Advances in optimization of mechanical properties in cast TiAl alloys // Intermetallics. 2005. Vol. 13, No. 9. Р. 914–919. 5. Hao Y. L., Yang R., Cui Y. Y., Li D. The influence of alloying on the α2/(α2 + γ)/γ-phase boundaries in TiAl based systems // Acta materialia. 2000. Vol. 48, No. 6. Р. 1313–1324. 6. Kainuma R., Fujita Y., Mitsui H., Ohnuma I., Ishida K. Phase equilibria among α (hcp), β (bcc) and γ (L10) phases in Ti – Al base ternary alloys // Intermetallics. 2000. Vol. 8, No. 8. P. 855–867. 7. Huang Z. W., Voice W., Bowen P. Thermal exposure induced α2+γ → B2(ω) and α2 → B2(ω) phase transformations in a high Nb fully lamellar TiAl alloy // Scripta Materialia. 2003. Vol. 48, No. 1. Р. 79–84. 8. Wang J. N., Xie K. Grain size refinement of a TiAl alloy by rapid heat treatment // Scripta Materialia. 2000. Vol. 43. P. 441–446. 9. Kuang J. P., Harding R. A., Campbell J. The effects of HIP pore closure and age hardening on primary creep and tensile property variations in a TiAl XD™ alloy with 0.1 wt. % carbon. Materials Science and Engineering: A. 2002. Vol. 31. pp. 321–331. 10. Huang A., Hu D., Loretto M. H., Mei J., Wu X. The influence of pressure on solid-state transformations in Ti – 46Al – 8Nb. Scripta Materialia. 2007. Vol. 56. pp. 253–256 11. Simpkins R. J., Rourke M. P., Bieler T. A., McQuayb P. A. The effect of HIP pore closure and age hardening on primary creep and tensile property variations in a TiAl XD alloy with 0.1 wt. % carbon. Materials Science Engineering: A. 2007. Vol. 463. pp. 208–215. 12. Güther V., Rothe C., Winter S., Clemens H. Metallurgy, microstructure and properties of intermetallic TiAl ingots. Berg and Hüttenmännische Monatshefte. 2010. Vol. 155. pp. 325–329. 13. Clemens H., Wallgram W., Kremmer S., Güther V., Otto A., Bartels A. Design of novel β-solidifying TiAl alloys with adjustable β/B2-phase fractionand excellent hot-workability. Advanced Engineering Materials. 2008. Vol. 10. pp. 707–713. 14. Clemens H., Mayer S. Design, processing, microstructure, properties, and applications of advanced intermetallic TiAl alloys. Advanced Engineering Materials. 2013. Vol. 15. pp. 191–215. 15. Clemens H., Chladil H. F., Wallgram W., Zickler G. A., Gerling R., Liss K. D., Kremmer S., Güther V., Smarsly W. In and ex situ investigations of the β-phase in a Nb and Mo containing γ-TiAl based alloy. Intermetallics. 2008. Vol. 16. pp. 827–833. 16. Ding Hongsheng, Nie Ge, Chen Ruirun, et al. Influence of oxygen on microstructure and mechanical properties of directionally solidified Ti – 47Al – 2Cr – 2Nb alloy. Materials & Design. 2012. Vol. 41. pp. 108–113. 17. Kartavykh A. V., Asnis E. A., Piskun N. V., Statkevich I. I., Gorshenkov M. V., Korotitskiy A. V. A promising microstructure/deformability adjustment of β-stabilized γ-TiAl intermetallics. Materials Letters. 2016. Vol. 162. pp. 180–184. 18. Huang Z. W. Thermal stability of Ti – 44Al – 4Nb – 4Zr – 0.2Si – 1B alloy. Intermetallics. 2013. Vol. 43. pp. 170–179. 19. Jiang H., Hu D., Wu X. Thermal stability of the omega phase in Zr-containing TiAl alloys. Journal of Alloys and Compounds. 2009. Vol. 475. pp. 134–138. 20. Lee D. B., Woo S. W., High temperature oxidation of Ti – 47%Al – 1.7%W – 3.7%Zr alloys. Intermetallics. 2005. Vol. 13. pp. 169–177. 21. GOST 2999–75. Metally i splavy. Metod izmereniya tverdosti po Vikkersu (State Standard 2999–75. Metals and alloys. Vickers hardness teat by diamond pyramid). Introduced : 1976–07–01. (in Russian) 22. Akopyan T. K., Padalko A. G., Belov N. A. Influence of hot isostatic pressing on the structure and properties of an innovative low-alloy highstrength aluminum cast alloy based on the Al – Zn – Mg – Cu – Ni – Fe system. Russian Metallurgy (Metally). 2015. Vol. 11. pp. 937–942. |