ArticleName Understanding the behaviour of aluminium alloy Р-1580 sparingly doped with scandium under hot deformation
DOI 10.17580/tsm.2019.09.13
ArticleAuthor Dovzhenko N. N., Rushchits S. V., Dovzhenko I. N., Yurev P. O.
ArticleAuthorData

Siberian Federal University, Krasnoyarsk, Russia:
N. N. Dovzhenko, Professor at the Department of Mechanical Engineering, e-mail: n.dovzhenko@bk.ru
I. N. Dovzhenko, Associate Professor at the Department of Metal Forming
P. O. Yurev, Applied Research Engineer

South Ural State University, Chelyabinsk, Russia:

S. V. Rushchits, Professor at the Department of Materials Science and Physics and Chemistry of Materials

Abstract

With the help of the Gleeble 3800 system, a study was carried out to understand the deformation behaviour of an experimental alloy Р-1580 sparingly doped with scandium. The alloy was designed by RUSAL UC (United Company) and contains the following doping elements (hereinafter — wt%): Al – 5 Mg – 0.6 Mn – 0.10 Sc – 0.11 Zr. The process involved uniaxial upse tting in the temperature range of 350–450 oC and the deformation rate range of 0.01–30 s–1. For the fixed temperatures of 350, 375, 400, 425 and 450 oC and deformation rates of 0.01, 0.1, 1, 10 and 30 s–1, experimental true stres s true strain curves were obtained for the alloy in view. At lower deformation rates (i.e. 0.01–1.0 s–1), the flow stresses reach a steady level corresponding to the equilibrium between strain hardening and softening (i. e. reco very) even after slight deformation. Deformation at higher rates (i. e. 10 and 30 s–1) leads to strain-induced heating of specimens, and as the strain rises the flow stresses drop. After the strain curves were adjusted to allow for the strain-induced heating, they started to look like curves typical of hot deformation controlled by dynamic recovery. These findings are perfectly in line with the popular belief that the combined effect of temperature and deformation rate on the deformation behaviour of metallic materials can be described with Zener-Hollomon parameter. Analytical expressions were derived for the steady flow stresses as a function of Zener-Hollomon parameter. They enable to predict plastic resistance of alloys within a wide range of temperatures and deformation rates. A curve was built that can help predict the rate coefficient as a function of a given temperature-rate regime of deformation.

keywords Aluminium alloys, physical modelling, Zener-Hollomon parameter, hot deformation, flow stress
References

1. Filatov Yu. A. Industrial alloys of the system Al – Mg – Sc. Tekhnologiya legkikh splavov. 1996. No. 3. pp. 30–35.
2. Gorbunov J. A. The Role and Prospects of Rare-Earth Metals in the Development of Physical-Mechanical Characteristics and Applications of Deformable Aluminum Alloys. Journal of Siberian Federal University. Engineering & Technologies. 2015. Vol. 8, No. 5. pp. 636–645.
3. Rushchits S., Aryshenskii E., Kawalla R., Serebryany V. Investigation of Texture Structure and Mechanical Properties Evolution during Hot Deformation of 1565 Aluminum Alloy. Materials Science Forum. 2016. Vol. 854. pp. 73–78. DOI: 10.4028/www.scientific.net/MSF.854.73
4. Filatov Yu. A. Wrought alloys of the system Al – Mg – Sc and their prospective application in car making. Tsvetnye Metally. 1997. No. 2. pp. 60–62.
5. Bronz A. V., Efremov V. I., Plotnikov A. D., Chernyavskiy A. G. 1570s — alloy for the tight structures of advanced reusable products made by the Rocket and Space Corporation Energiya. Space Engineering and Technology. 2014. No. 4 (7). pp. 62–67.
6. Baranov V. N., Sidelnikov S. B., Zenkin E. Yu., Voroshilov D. S. Developing regimes for obtaining deformed semi-finished products made of experimental scandium-containing aluminium alloy and understanding their mechanical properties. Izvestiya vuzov. Tsvetnaya metallurgiya. 2018. No. 2. pp. 43–49.
7. Dovzhenko I. N., Dovzhenko N. N., Sidelnikov S. B., Konstantinov I. L. 3D modelling of the large-capacity ingots of an Al – Mg system aluminium alloy doped with scandium rolling process. Non-ferrous Metals. 2017. No. 2. pp. 60–64.
8. Churyumova A. Yu., Teleshov V. V. On quantitative description of the relationship between the flow stress of aluminium alloys at the equilibrium flow stage during hot deformation and Zener-Hollomon parameter. Fizika metallov i metallovedenie. 2017. Vol. 118, No. 9. pp. 950–957.
9. Sellars C. M., Tegart W. J., McG. La relation entre la résistance et la structure dans la deformation à chaud. Mémoires scientifiques de la Revue de métallurgie. 1966. Vol. 63. pp. 731–746.
10. Chen S.-R., Wu C.-Y., Yeh Y.-L., Ou Y.-L. Hot Deformation Resistance of an AA5083 Alloy under High Strain Rates. China Steel Technical Report. 2014. No. 27. pp. 83–88.
11. Rushchits S. V., Aryshenskiy E. V., Sosedkov S. M., Akhmedyanov A. M. Modeling the Hot Deformation Behavior of 1565ch Aluminum Alloy. Key Engineering Materials. 2016. Vol. 684. pp. 35–41.

Language of full-text russian
Full content Buy
Back