ArticleName Understanding the structure and properties of the heat affected zone in welds and model specimens of high-strength low-alloy steels after simulated heat cycles
DOI 10.17580/cisisr.2020.01.12
ArticleAuthor E. I. Pryakhin, D. M. Sharapova
ArticleAuthorData

St. Petersburg Mining University (St. Petersburg, Russia):

E. I. Pryakhin, Dr. Eng., Prof., Head of Dept. of Material Science, E-mail: e.p.mazernbc@yandex.ru
D. M. Sharapova, Cand. Eng., Assistant

Abstract

Localized heat applied during welding or rebuilding of parts can lead to a noticeable structural evolution in the heat affected zone of the high-strength low-alloy K65 steel. A comprehensive study that was carried out on model and full-scale specimens and looked at the structure and properties of steel in the heat affected zone after single and double heat cycles proved the above trend. Through metallographic and X-ray microstructural analysis, it was found how and in what conditions a brittle phase forms at coarse grain boundaries, the amount of which and the distribution around the grain is in direct relationship with the number of heat cycles and the heat input of the welding procedure. It was established that during the initial heat cycle the new phase around the grains tends to grow as the cooling rate goes down, which is consistent with the reduced toughness of steel in the heat affected zone during high heat input welding. When the HAZ is reheated, the undesirable structural changes become even more pronounced. The results of the study show that the steel in view does not provide enough workability and that a specification is required to limit the amount of heat input introduced during the initial and further heat cycles in welding.

keywords Low-alloy high-strength steel, electric arc welding, reheating, heat affected zone, microstructure, dilatometric study, impact energy, heat input
References

1. Shchipachev A. M., Gorbachev S. V. Effect of post weld heat treatment on the rate of general corrosion and the microstructure of weld joints on Steel 20 and Steel 30KhGSA. Zapiski Gornogo instituta. 2018. Vol. 231. pp. 307–311.
2. Kirian V. I., Mikhoduy L. I. Problems related to the use of new extra-high and high strength steels in welded structures. Avtomaticheskaya svarka. 2002. No. 3. pp. 10–17.
3. Golosienko S. A., Ilyin A. V., Lavrentiev A. A., Mikhailov M. S., Motovilina G. D., Petrov S. N., Sadkin K. E. Brittle fracture resistance of high-strength medium-alloy steel and how it is related to the structural state parameters. Voprosy materialovedeniya. 2019. No. 3 (99). pp. 128–147.
4. Velichko A. A., Bortsov A. N., Shabalov I. P., Frantov I. I., Utkin I. Yu. Relationship between heat processes and the weld morphology and innovative welding techniques applicable to thick-walled electric-welded pipes. Metallurg. 2014. No. 3. pp. 72–77.
5. Thiessen R. G., Paul G., Sebald R. Innovative high-strength steels with enhanced mechanical parameters. Chernye Metally. 2019. No. 8. pp. 51–55.
6. Oryshchenko A. S., Pimenov A.V., Shekin S. I., Sharapov M. G. Understanding the effect of nonmetallic inclusions on the weld toughness of cold-resistant steels at low temperatures. Svarochnoe proizvodstvo. 2012. No. 8. pp. 6–11.
7. Hamada M. Control of strength and toughness at the heat affected zone. Welding International. 2003. No. 17(4). pp. 265–270.
8. Shi Y., Han Z. Effect of weld thermal cycle on microstructure and fracture toughness of simulated heat-affected zone for a 800 MPa grade high strength low alloy steel. Journal of Materials Processing Technology. 2008. Vol. 207. pp. 30–39.
9. Hillenbrand H.-G., Gras M., Kalwa C. Development and production of high strength pipeline steels. Niobium Science and Technology: Proceedings of the International Symposium on Niobium. Orlando, Florida. 2001, Dec. 2–5.
10. Meimeth S., Grimpe F., Meuser H. Development, state of the art and future trends in design and production of heavy plates in X80 steel grades. Steel Rolling 2006, 9th International & 4th European Conferences. Paris, France. 2006, June 19–21.
11. Shkatov V. V., Mazur I. P., Knapinski M., Chetverikova T. S. Simulation of dynamic recrystallization and resistance to deformation of carbon and low-alloyed steels during hot forming. Chernye Metally. 2018. No. 11. pp. 22–27.
12. Erofeev V. A., Maslennikov A. V. Multipass arc welding procedure and its physico-mathematical model. Izvestiya Tulskogo gosudarstvennogo universiteta. Seriya: Kompyuternye tekhnologii v soedinenii materialov. 2005. No. 3. pp. 246–255.
13. Ueda J., Muracawa H., Luo Ju. A. Computational model of phase transformation for welding processes. Translation of JWRI. 1995. Vol. 24. No. 1, pp. 95–100.
14. Rao R. V., Kalyankar V.D. Multi-pass turning process parameter optimization using teaching–learning-based optimization algorithm. Scientia Iranica. 2013. Vol. 20. Issue 3. pp. 967–974.
15. Makarchuk A. V., Makarchuk N. V., Startsev V. N. Multipass arc welding procedure: Developing a mathematical model. Vestnik gosudarstvennogo universiteta morskogo i rechnogo flota imeni admirala S. O. Makarova. 2017. Vol. 9. No. 1. pp. 121–131.
16. Zubchenko A. S., Fedorov A. V., Nechaev Yu. V. Understanding what causes cracking of weld joints on thick-walled pressure vessel under further heat treatment. Svarka i diagnostika. 2009. No. 2. pp. 21–25.

Full content Understanding the structure and properties of the heat affected zone in welds and model specimens of high-strength low-alloy steels after simulated heat cycles
Back