The diagram of recrystallization has been built using conditions of hot rolling of strip from zink-titanium alloy, received on the base of the results of physical simulation at the quatro 400/1000x1000 mill from Moscow plants of processing of non-ferrous metals. This diagram also used obtained data of Vickers hardness values, calculated their average value, root-mean-square deviations, variations of distribution and qualitative metallographic analysis. The equations of flat boundes of diagram, divided the following areas: recovery and polygonization; primary recrystallization; recrystallized state are obtained in rectifying volume. On the base of conducted researches it has been devised the order of hot rolling of field from zink-titanium alloy on the quatro 400/1000x1000 reverse mill, providing the derivation of ready field, usable for sheet-metal forming without additional baking.